ACRYLITE? Hi-Gloss NTA-5 black is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA).
Properties
ACRYLITE? molding compounds have the following typical properties:
ACRYLITE? Hi-Gloss NTA-5 black is characterized by the following additional properties:
Application areas are:
Add-on automotive body parts, pillar-trims, mirror housings, trim parts at front - and rear end, etc.
添加劑 | |
特性 | - 沖擊改性、高光、高強(qiáng)度、抗撞擊性高、可回收材料、耐氣候影響性能良好、無定形的
|
用途 | - 汽車領(lǐng)域的應(yīng)用、汽車外部裝飾
|
機(jī)構(gòu)評級 | |
外觀 | |
形式 | |
加工方法 | |
密度 | 1.16 | g/cm3 | ISO 1183 |
熔融體積流量（MVR） |
|
| ISO 1133 |
230°C/3.8 kg | 0.0793 | in3/10min |
|
260°C/3.8 kg | 0.488 | in3/10min |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 1.5 | % |
|
平衡, 73°F, 50% RH | 0.50 | % |
|
拉伸模量 | 305000 | psi | ISO 527-2/1 |
拉伸應(yīng)力 (屈服) | 7830 | psi | ISO 527-2/50 |
拉伸應(yīng)變 (屈服) | 5.0 | % | ISO 527-2/50 |
標(biāo)稱拉伸斷裂應(yīng)變 | 48 | % | ISO 527-2 |
簡支梁無缺口沖擊強(qiáng)度 (73°F) | 52 | ft·lb/in2 | ISO 179/1eU |
熱變形溫度 |
|
|
|
66 psi, 未退火 | 216 | °F | ISO 75-2/B |
264 psi, 未退火 | 205 | °F | ISO 75-2/A |
玻璃轉(zhuǎn)化溫度 | 235 | °F | ISO 11357-2 |
維卡軟化溫度 | 217 | °F | ISO 306/B50 |
線形熱膨脹系數(shù) - 流動 (32 到 122°F) | 6.1E-5 | in/in/°F | ISO 11359-2 |
UL 阻燃等級 (0.06 in) | HB |
| IEC 707 |
干燥溫度 | 176 | °F |
|
干燥時間 | > 4.0 | hr |
|
加工（熔體）溫度 | 446 到 500 | °F |
|
模具溫度 | 140 到 176 | °F |
|