CYCOLAC? Resin EX58
丙烯腈丁二烯苯乙烯
產品說明:
High impact ABS for sheet extrusion and blow molding applications.
密度 / 比重 |
|
|
|
-- | 1.03 |
| ASTM D792 |
-- | 1.03 | g/cm3 | ISO 1183 |
熔流率（熔體流動速率） (220°C/10.0 kg) | 4.0 | g/10 min | ISO 1133 |
收縮率 - 流動 (0.126 in) | 6.0E-3 到 8.0E-3 | in/in | 內部方法 |
洛氏硬度 (R 級) | 102 |
| ASTM D785 |
拉伸模量 |
|
|
|
-- 2 | 302000 | psi | ASTM D638 |
-- | 286000 | psi | ISO 527-2/1 |
抗張強度 |
|
|
|
屈服 3 | 5660 | psi | ASTM D638 |
屈服 | 5950 | psi | ISO 527-2/50 |
斷裂 3 | 4350 | psi | ASTM D638 |
斷裂 | 4350 | psi | ISO 527-2/50 |
伸長率 |
|
|
|
屈服 3 | 3.1 | % | ASTM D638 |
屈服 | 2.6 | % | ISO 527-2/50 |
斷裂 3 | 32 | % | ASTM D638 |
斷裂 | 21 | % | ISO 527-2/50 |
彎曲模量 |
|
|
|
1.97 in 跨距 4 | 313000 | psi | ASTM D790 |
-- 5 | 290000 | psi | ISO 178 |
彎曲應力 |
|
|
|
-- 5, 6 | 8700 | psi | ISO 178 |
屈服, 1.97 in 跨距 4 | 9570 | psi | ASTM D790 |
簡支梁缺口沖擊強度 7 (73°F) | 18 | ft·lb/in2 | ISO 179/1eA |
懸壁梁缺口沖擊強度 |
|
|
|
-22°F | 5.6 | ft·lb/in | ASTM D256 |
73°F | 8.1 | ft·lb/in | ASTM D256 |
-22°F 8 | 11 | ft·lb/in2 | ISO 180/1A |
73°F 8 | 17 | ft·lb/in2 | ISO 180/1A |
裝有測量儀表的落鏢沖擊 (73°F, Total Energy) | 327 | in·lb | ASTM D3763 |
載荷下熱變形溫度 |
|
|
|
66 psi, 未退火, 0.126 in | 196 | °F | ASTM D648 |
264 psi, 未退火, 0.126 in | 169 | °F | ASTM D648 |
264 psi, 未退火, 2.52 in 跨距 9 | 172 | °F | ISO 75-2/Af |
維卡軟化溫度 |
|
|
|
-- | 223 | °F | ASTM D1525 10 |
-- | 203 | °F | ISO 306/B50 |
-- | 207 | °F | ISO 306/B120 |
線形熱膨脹系數 |
|
| ASTM E831 |
流動 : -40 到 104°F | 5.6E-5 | in/in/°F |
|
橫向 : -40 到 104°F | 5.8E-5 | in/in/°F |
|
RTI Elec | 140 | °F | UL 746 |
RTI Imp | 140 | °F | UL 746 |
RTI | 140 | °F | UL 746 |
耐電弧性 11 | PLC 5 |
| ASTM D495 |
相比耐漏電起痕指數(CTI) | PLC 0 |
| UL 746 |
高電弧燃燒指數(HAI) | PLC 4 |
| UL 746 |
高電壓電弧起痕速率 (HVTR) | PLC 1 |
| UL 746 |
熱絲引燃 (HWI) | PLC 4 |
| UL 746 |
UL 阻燃等級 (0.06 in) | HB |
| UL 94 |
熔體粘度 (464°F, 100 sec^-1) | 1550 | Pa·s | ASTM D3835 |
Extrusion Blow Molding Parameters: Sheet Extrusion Parameters: |
如需沙伯基礎（SABIC）原廠物性表及相關文件，請聯系我們工作人員，謝謝！