Elastollan? 890AN
熱塑性聚氨酯彈性體（聚酯）
產品說明:
Elastollan? 890AN is specifically formulated for transparent film applications. It exhibits excellent abrasion resistance, toughness, transparency, and oil/fuel resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan?890AN conforms to the FDA food contact regulations as described in book 21, section 177.2600 and 177.1680 for both wet and dry food contact applications respectively. Elastollan? 890AN is supplied uncolored in pellet form.
機構評級 | FDA 21 CFR 177.1680、FDA 21 CFR 177.2600 |
外觀 | |
加工方法 | 擠出、注射成型 |
密度 / 比重 | 1.22 |
| ASTM D792 |
熔流率（熔體流動速率） (190°C/8.7 kg) | 15 到 30 | g/10 min | ASTM D1238 |
肖氏硬度 (邵氏 A) | 92 |
| ASTM D2240 |
拉伸模量 (注塑) | 4200 | psi | ASTM D412 |
彎曲模量 (注塑) | 9700 | psi | ASTM D790 |
泰伯耐磨性 | 45.0 | mg | ASTM D1044 |
Abrasion - DIN | 25 | mm3 | DIN 53516 |
拉伸應力 |
|
| ASTM D412 |
100%應變 | 2000 | psi |
|
300%應變 | 4500 | psi |
|
抗張強度 | 5700 | psi | ASTM D412 |
伸長率 (斷裂) | 480 | % | ASTM D412 |
撕裂強度 2 | 820 | lbf/in | ASTM D624 |
壓縮永久變形 |
|
| ASTM D395B |
73°F, 22 hr | 20 | % |
|
158°F, 22 hr | 45 | % |
|
玻璃轉化溫度 | 6.80 | °F | 內部方法 |
維卡軟化溫度 | 248 | °F | ASTM D1525 |
Softening Point - DMA | 178 | °F | 內部方法 |
干燥溫度 | 230 到 248 | °F |
|
干燥時間 | 2.0 到 3.0 | hr |
|
建議的最大水分含量 | 0.030 | % |
|
料筒后部溫度 | 374 到 428 | °F |
|
料筒中部溫度 | 374 到 428 | °F |
|
料筒前部溫度 | 374 到 428 | °F |
|
射嘴溫度 | 410 到 437 | °F |
|
干燥溫度 | 230 到 248 | °F |
|
干燥時間 | 2.0 到 3.0 | hr |
|
料筒1區溫度 | 338 到 410 | °F |
|
料筒3區溫度 | 338 到 410 | °F |
|
料筒5區溫度 | 338 到 410 | °F |
|
接頭溫度 | 392 到 428 | °F |
|
口模溫度 | 383 到 419 | °F |
|
如需巴斯夫原廠物性表及相關文件，請聯系我們工作人員，謝謝！