Akulon? F132
聚酰胺6
產(chǎn)品說明:
Film Extrusion, High Viscosity
Special Features:
Akulon? is our family of high performance polyamide 6 and polyamide 66 materials, used by customers across the world in applications ranging from automotive, electronics & electrical, to furniture and packaging.
We offer Akulon? grades for injection molding, blow molding and extrusion (including barrier film, stock shapes, convoluted tubes, and mono and multi filament).
In molded parts the material offers an excellent balance of easy design and processing with outstanding mechanical properties over a wide temperature range and in diverse conditions. Meanwhile for extrusion the strength, resilience and easy processing of Akulon? sets the market standards.
特性 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | |
樹脂ID (ISO 1043) | |
密度 | 1.13 | g/cm3 | ISO 1183 |
吸水率 |
|
| ISO 62 |
飽和, 73°F | 9.5 | % |
|
平衡, 73°F, 50% RH | 2.5 | % |
|
粘數(shù) | 210 | cm3/g | ISO 307 |
摩擦系數(shù) |
|
| ISO 8295 |
Dynamic | 1.0 |
|
|
Static | 1.2 |
|
|
拉伸模量 2 | 65300 | psi | 內(nèi)部方法 |
拉伸應(yīng)力 - MD |
|
| ISO 527-3 |
屈服 | 4640 | psi |
|
斷裂 | 12000 | psi |
|
伸長率 - MD (斷裂) | 350 | % | ISO 527-3 |
Trouser Tear - Parallel | 32.0 |
| ISO 6383-1 |
水氣透過率 (73°F, 85% RH) | 2.3 | g/100 in2/24 hr | DIS 15106-1/-3 |
氧氣傳輸速率 |
|
| DIS 15105-1/-2 |
0% RH : 73°F | 26 | cm3/m2/bar/24 hr |
|
85% RH : 73°F | 38 | cm3/m2/bar/24 hr |
|
熔融溫度 3 | 428 | °F | ISO 11357-3 |
線形熱膨脹系數(shù) - 流動(dòng) | 5.0E-5 | in/in/°F | ISO 11359-2 |
Specific Heat Capacity | 0.370 | Btu/lb/°F |
|
熔體粘度 (500°F) | 1.12E+6 | mPa·s | 內(nèi)部方法 |
Average Specific Heat Capacity (68 到 302°F) | 0.609 | Btu/lb/°F |
|
Puncture Resistance | 24.4 | ft·lb/in | 內(nèi)部方法 |
RSV - Formic Acid, 1g/100ml | 3.20 |
| 內(nèi)部方法 |
干燥溫度 | 176 | °F |
|
干燥時(shí)間 | 4.0 到 8.0 | hr |
|
料筒后部溫度 | 446 到 455 | °F |
|
料筒中部溫度 | 455 到 482 | °F |
|
料筒前部溫度 | 464 到 500 | °F |
|
射嘴溫度 | 464 到 518 | °F |
|
加工（熔體）溫度 | 464 到 527 | °F |
|
模具溫度 | 122 到 176 | °F |
|
注射速度 | 中等偏快 |
|
|
背壓 | 435 到 1450 | psi |
|
螺桿壓縮比 | 2.5:1.0 |
|
|
如需恩驊力（Envalior）原廠物性表及相關(guān)文件，請聯(lián)系我司工作人員，謝謝！