ForTii? F11C
Polyamide 4T
產品說明:
30% Glass Reinforced, Flame Retardant, Halogen free and free of red phosphorous, Improved color stability
Special Features:
Used In:
ForTii? is a breakthrough high temperature polyamide with halogen-free flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries.
We developed ForTii? in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want €" and need.
That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.
填料/增強材料 | |
添加劑 | |
特性 | |
用途 | |
加工方法 | |
樹脂ID (ISO 1043) | |
密度 | 1.46 | -- | g/cm3 | ISO 1183 |
收縮率 |
|
|
| ISO 294-4 |
橫向流量 | 1.2 | -- | % |
|
流量 | 0.30 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
飽和, 73°F | 4.6 | -- | % |
|
平衡, 73°F, 50% RH | 1.6 | -- | % |
|
粘數 | 86.0 | -- | cm3/g | ISO 307 |
拉伸模量 |
|
|
| ISO 527-2 |
-- | 1.74E+6 | 1.74E+6 | psi |
|
248°F | 1.16E+6 | -- | psi |
|
320°F | 798000 | -- | psi |
|
拉伸應力 |
|
|
| ISO 527-2 |
斷裂 | 22500 | 22500 | psi |
|
斷裂, 248°F | 15200 | -- | psi |
|
斷裂, 320°F | 10900 | -- | psi |
|
拉伸應變 |
|
|
| ISO 527-2 |
斷裂 | 2.0 | 2.0 | % |
|
斷裂, 248°F | 2.7 | -- | % |
|
斷裂, 320°F | 3.7 | -- | % |
|
彎曲模量 | 1.67E+6 | 1.67E+6 | psi | ISO 178 |
彎曲應力 | 35500 | 33400 | psi | ISO 178 |
簡支梁缺口沖擊強度 (73°F) | 4.8 | 4.8 | ft·lb/in2 | ISO 179/1eA |
簡支梁無缺口沖擊強度 (73°F) | 24 | 24 | ft·lb/in2 | ISO 179/1eU |
熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 613 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 581 | -- | °F | ISO 75-2/A |
玻璃轉化溫度 3 | 257 | -- | °F | ISO 11357-2 |
熔融溫度 3 | 617 | -- | °F | ISO 11357-3 |
線形熱膨脹系數 |
|
|
| ASTM D696 |
流動 | 1.7E-5 | -- | in/in/°F |
|
橫向 | 1.9E-5 | -- | in/in/°F |
|
RTI Elec (0.0079 in) | 239 | -- | °F | UL 746 |
介電強度 | 840 | 840 | V/mil | IEC 60243-1 |
相對電容率 |
|
|
| IEC 60250 |
100 Hz | 4.20 | 4.20 |
|
|
1 MHz | 3.90 | 3.90 |
|
|
1.00 GHz | 3.90 | 3.90 |
|
|
10.0 GHz | 3.90 | 3.80 |
|
|
耗散因數 |
|
|
| IEC 60250 |
100 Hz | 6.4E-3 | 6.4E-3 |
|
|
1 MHz | 0.018 | 0.018 |
|
|
漏電起痕指數 | 600 | -- | V | IEC 60112 |
可燃性等級 |
|
|
| IEC 60695-11-10, -20 |
0.0079 in | V-0 | -- |
|
|
0.06 in | V-0 | -- |
|
|
極限氧指數 | 39 | -- | % | ISO 4589-2 |
干燥溫度 | 212 | °F |
|
干燥時間 | 4.0 到 8.0 | hr |
|
料筒后部溫度 | 608 到 626 | °F |
|
料筒中部溫度 | 617 到 635 | °F |
|
料筒前部溫度 | 626 到 635 | °F |
|
射嘴溫度 | 626 到 635 | °F |
|
加工（熔體）溫度 | 626 到 644 | °F |
|
模具溫度 | 212 到 302 | °F |
|
注射速度 | 中等偏快 |
|
|
背壓 | 72.5 到 435 | psi |
|
螺桿壓縮比 | 2.5:1.0 |
|
|
如需恩驊力（Envalior）原廠物性表及相關文件，請聯系我司工作人員，謝謝！