Texin? 288
熱塑性聚氨酯彈性體（聚酯）
Texin 288 is an aromatic polyester-based thermoplastic polyurethane with a hardness of approximately 88A. It can be processed by injection molding. Extrusion processes are also possible for some applications.
特性 | - 抗撞擊性，良好、良好的柔韌性、良好耐磨損性、耐低溫、耐燃油性、耐油性能、韌性良好
|
用途 | |
加工方法 | |
密度 / 比重 |
|
|
|
-- | 1.20 |
| ASTM D792 |
-- | 1.20 | g/cm3 | ISO 1183 |
收縮率 |
|
|
|
流動 : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
橫向流動 : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
橫向流量 : 0.100 in | 0.80 | % | ISO 2577 |
流量 : 0.100 in | 0.80 | % | ISO 2577 |
肖氏硬度 |
|
| ASTM D2240, ISO 868 |
邵氏 A | 88 |
|
|
邵氏 D | 38 |
|
|
彎曲模量 (73°F) | 6700 | psi | ASTM D790, ISO 178 |
泰伯耐磨性 |
|
|
|
1000 Cycles, 1000 g, H-18 轉輪 | 40.0 | mg | ASTM D1044 |
1000 Cycles, 1000 g, H-18 轉輪 | 40.0 | mg | ISO 4649 |
拉伸應力 |
|
| ASTM D412, ISO 37 |
100%應變 | 1000 | psi |
|
300%應變 | 2900 | psi |
|
抗張強度 (屈服) | 6800 | psi | ASTM D412, ISO 37 |
伸長率 (斷裂) | 500 | % | ASTM D412, ISO 37 |
撕裂強度 |
|
|
|
-- 2 | 600 | lbf/in | ASTM D624 |
-- | 600 | lbf/in | ISO 34-1 |
壓縮永久變形 |
|
| ISO 815 |
73°F, 22 hr | 15 | % | ASTM D395 |
73°F, 22 hr 3 | 12 | % | ASTM D395B |
158°F, 22 hr | 52 | % | ASTM D395 |
158°F, 22 hr 3 | 21 | % | ASTM D395B |
巴肖氏彈性 | 41 | % | ASTM D2632 |
玻璃轉化溫度 | -49.0 | °F | DMA |
維卡軟化溫度 | 275 | °F | ISO 306/A50, ASTM D1525 4 |
干燥溫度 - 熱風干燥機 | 210 到 230 | °F |
|
干燥時間 - 熱風干燥機 | 2.0 | hr |
|
建議的最大水分含量 | < 0.030 | % |
|
建議的最大回制料比例 | 20 | % |
|
料筒后部溫度 | 374 到 410 | °F |
|
料筒中部溫度 | 374 到 419 | °F |
|
料筒前部溫度 | 392 到 428 | °F |
|
射嘴溫度 | 401 到 437 | °F |
|
加工（熔體）溫度 | 401 到 419 | °F |
|
模具溫度 | 59 到 104 | °F |
|
注塑壓力 | 6000 到 15000 | psi |
|
注射速度 | 慢到中等 |
|
|
背壓 | < 200 | psi |
|
螺桿轉速 | 40 到 80 | rpm |
|
墊層 | < 0.125 | in |
|