Texin? 250
熱塑性聚氨酯彈性體（聚酯）
Texin 250 resin is an aromatic polyester-based thermoplastic polyurethane with a Shore hardness of approximately 50D. It is processed primarily by extrusion and blow molding but can also be used for injection molding.
特性 | - 低速凝固晶點、抗溶劑性、良好耐磨損性、耐化學性良好、耐油性能、中等透明度
|
用途 | |
機構評級 | - FDA 21 CFR 177.1680FDA 21 CFR 177.2600
|
外觀 | |
加工方法 | |
密度 / 比重 |
|
|
|
-- | 1.22 |
| ASTM D792 |
-- | 1.22 | g/cm3 | ISO 1183 |
收縮率 |
|
|
|
流動 : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
橫向流動 : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
橫向流量 : 0.100 in | 0.80 | % | ISO 2577 |
流量 : 0.100 in | 0.80 | % | ISO 2577 |
肖氏硬度 |
|
| ASTM D2240, ISO 868 |
邵氏 A | 95 |
|
|
邵氏 D | 50 |
|
|
彎曲模量 |
|
| ASTM D790, ISO 178 |
73°F | 12000 | psi |
|
158°F | 5220 | psi |
|
泰伯耐磨性 |
|
|
|
1000 Cycles, 1000 g, H-18 轉輪 | 70.0 | mg | ASTM D1044 |
1000 Cycles, 1000 g, H-18 轉輪 | 70.0 | mg | ISO 4649 |
拉伸應力 |
|
| ASTM D412, ISO 37 |
100%應變 | 1700 | psi |
|
300%應變 | 4600 | psi |
|
抗張強度 (屈服) | 6700 | psi | ASTM D412, ISO 37 |
伸長率 (斷裂) | 400 | % | ASTM D412, ISO 37 |
撕裂強度 |
|
|
|
-- 2 | 775 | lbf/in | ASTM D624 |
-- | 780 | lbf/in | ISO 34-1 |
壓縮永久變形 3 |
|
| ASTM D395B, ISO 815 |
73°F, 22 hr | 15 | % |
|
158°F, 22 hr | 35 | % |
|
巴肖氏彈性 | 25 | % | ASTM D2632 |
玻璃轉化溫度 | -4.00 | °F | DMA |
維卡軟化溫度 | 239 | °F | ISO 306/A50, ASTM D1525 4 |
干燥溫度 - 熱風干燥機 | 199 到 219 | °F |
|
干燥時間 - 熱風干燥機 | 2.0 | hr |
|
建議的最大水分含量 | 0.030 | % |
|
建議的最大回制料比例 | 20 | % |
|
料筒后部溫度 | 374 到 410 | °F |
|
料筒中部溫度 | 374 到 419 | °F |
|
料筒前部溫度 | 392 到 428 | °F |
|
射嘴溫度 | 401 到 437 | °F |
|
加工（熔體）溫度 | 401 到 419 | °F |
|
模具溫度 | 59 到 104 | °F |
|
注塑壓力 | 6000 到 15000 | psi |
|
注射速度 | 慢到中等 |
|
|
背壓 | < 200 | psi |
|
螺桿轉速 | 40 到 80 | rpm |
|
墊層 | 0.125 | in |
|
Hold Pressure: 60 to 80% of Injection Pressure |
干燥溫度 | 199 到 219 | °F |
|
干燥時間 | 2.0 | hr |
|
建議的最大回制料比例 | 20 | % |
|
料筒1區溫度 | 356 到 392 | °F |
|
料筒3區溫度 | 356 到 401 | °F |
|
料筒5區溫度 | 356 到 410 | °F |
|
熔體溫度 | 374 到 401 | °F |
|
口模溫度 | 365 到 410 | °F |
|