Desmopan? 460
熱塑性聚氨酯彈性體（聚酯）
injection molding grade; grease and oil-resistant; low compression set; good heat resistance; high elasticity; short cycle times; Application; Automotive engineering; Technical parts; Bearing bushes
特性 | - 低的壓縮變形性、高彈性、快的成型周期、耐熱性高、耐油性能、耐油脂性能
|
用途 | |
RoHS 合規性 | |
加工方法 | |
多點數據 | Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
|
密度 |
|
|
|
73°F | 1.22 | g/cm3 | ISO 1183 |
-- | 0.0441 | lb/in3 | ISO 1183 3 |
肖氏硬度 |
|
|
|
邵氏 A, 1 秒, 73°F | 97 |
| ISO 7619 |
邵氏 D, 1 秒, 73°F | 59 |
| ISO 7619 |
邵氏 A, 3 sec | 97 |
| ISO 868 3 |
邵氏 D, 15 sec | 59 |
| ISO 868 3 |
拉伸應力 4 |
|
| DIN 53504 |
斷裂, 73°F | 6160 | psi |
|
10% 應變, 73°F | 2190 | psi |
|
50% 應變, 73°F | 3260 | psi |
|
300% 應變, 73°F | 5090 | psi |
|
拉伸應變 4 (斷裂, 73°F) | 390 | % | DIN 53504 |
彎曲模量 5 (73°F) | 24700 | psi | ISO 178 |
Tensile Storage Modulus |
|
| ISO 6721 |
-4°F | 255 | ksi |
|
68°F | 64.7 | ksi |
|
140°F | 18.9 | ksi |
|
抗磨損性 6 | 40.0 | mm3 | ISO 4649 |
撕裂強度 7 (73°F) | 860 | lbf/in | ISO 34-1 |
壓縮永久變形 |
|
| ISO 815 |
73°F, 72 hr | 25 | % |
|
158°F, 24 hr 6 | 32 | % |
|
158°F, 24 hr 8 | 21 | % |
|
Rebound Resilience | 35 | % | ISO 4662 |
干燥溫度 | < 230 | °F |
|
加工（熔體）溫度 | 455 到 473 | °F |
|
模具溫度 | 68 到 104 | °F |
|