Desmopan? 3385A
熱塑性聚氨酯彈性體（聚酯）
Extrusion- and injection molding grade; good wear resistance; short cycle times; high melt stability; Application; hard - soft systems; Hoses, non-reinforced; Profiles; Injection molded engineering parts
密度 |
|
|
|
73°F | 1.20 | g/cm3 | ISO 1183 |
-- | 0.0434 | lb/in3 | ISO 1183 2 |
肖氏硬度 |
|
|
|
邵氏 A, 1 秒, 73°F | 85 |
| ISO 7619 |
邵氏 D, 1 秒, 73°F | 33 |
| ISO 7619 |
邵氏 A, 3 sec | 85 |
| ISO 868 2 |
邵氏 D, 15 sec | 33 |
| ISO 868 2 |
拉伸應力 3 |
|
| DIN 53504 |
斷裂, 73°F | 7540 | psi |
|
10% 應變, 73°F | 290 | psi |
|
50% 應變, 73°F | 682 | psi |
|
100% 應變, 73°F | 841 | psi |
|
300% 應變, 73°F | 2410 | psi |
|
拉伸應變 3 (斷裂, 73°F) | 530 | % | DIN 53504 |
Tensile Storage Modulus |
|
| ISO 6721 |
-4°F | 12183 | psi |
|
68°F | 4061 | psi |
|
140°F | 3046 | psi |
|
抗磨損性 4 | 25.0 | mm3 | ISO 4649 |
撕裂強度 5 (73°F) | 400 | lbf/in | ISO 34-1 |
壓縮永久變形 |
|
| ISO 815 |
73°F, 72 hr | 15 | % |
|
158°F, 24 hr 4 | 42 | % |
|
Rebound Resilience | 50 | % | ISO 4662 |
干燥溫度 | < 176 | °F |
|
加工（熔體）溫度 | 374 到 410 | °F |
|
模具溫度 | 68 | °F |
|
干燥溫度 | < 176 | °F |
|
熔體溫度 | 347 到 401 | °F |
|
如需科思創原廠物性表及相關文件，請聯系我們工作人員，謝謝！