VESTAMID? L L1833
聚酰胺12
Reinforced, filled and flame-retardant VESTAMID? polyamide 12 compounds
Characterization: 23% chopped strands, medium viscosity, heat stabilized with processing aid
Applications: connectors for fuel lines
In general, it can be said that long-chain, semi-crystalline polyamides absorb little water, are resistant to polar and non-polar solvents, exhibit low creep behavior and high impact resistance and can be used in a wide temperature range. Virtually no other polymer material in this price range exhibits these properties.
填料/增強材料 | |
添加劑 | |
特性 | Excellent Processability、半結(jié)晶、低摩擦系數(shù)、高 ESCR（抗應(yīng)力開裂）、減震、降噪、 抗溶劑性、抗撞擊性高、良好耐磨損性、耐低溫沖擊、耐疲勞性能、耐燃油性、耐油性能、 耐油脂性能、熱穩(wěn)定性、食品接觸的合規(guī)性、吸水低或不吸水、中等粘性
|
用途 | |
機構(gòu)評級 | - FDA 21 CFR 177.1500、歐洲 10/1/2011 12:00:00 AM
|
外觀 | |
形式 | |
加工方法 | |
密度 | 1.17 | g/cm3 | ISO 1183 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 0.65 | % |
|
流量 | 0.20 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 1.2 | % |
|
平衡, 73°F, 50% RH | 0.60 | % |
|
拉伸模量 | 725000 | psi | ISO 527-2 |
拉伸應(yīng)力 (斷裂) | 15200 | psi | ISO 527-2 |
拉伸應(yīng)變 (斷裂) | 6.0 | % | ISO 527-2 |
簡支梁缺口沖擊強度 |
|
| ISO 179/1eA |
-22°F, 完全斷裂 | 7.6 | ft·lb/in2 |
|
73°F, 完全斷裂 | 12 | ft·lb/in2 |
|
簡支梁無缺口沖擊強度 |
|
| ISO 179/1eU |
-22°F, 完全斷裂 | 45 | ft·lb/in2 |
|
73°F, 完全斷裂 | 43 | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
66 psi, 未退火 | 347 | °F | ISO 75-2/B |
264 psi, 未退火 | 320 | °F | ISO 75-2/A |
維卡軟化溫度 | 347 | °F | ISO 306/A, ISO 306/B |
熔融溫度 3 | 352 | °F | ISO 11357-3 |
線形熱膨脹系數(shù) - 流動 (73 到 131°F) | 3.9E-5 | in/in/°F | ISO 11359-2 |
體積電阻率 | 1.0E+15 | ohms·cm | IEC 60093 |
介電強度 | 1000 | V/mil | IEC 60243-1 |
相對電容率 |
|
| IEC 60250 |
73°F, 100 Hz | 4.10 |
|
|
73°F, 1 MHz | 3.40 |
|
|
耗散因數(shù) |
|
| IEC 60250 |
73°F, 100 Hz | 0.037 |
|
|
73°F, 1 MHz | 0.026 |
|
|
漏電起痕指數(shù) |
|
| IEC 60112 |
-- | 600 | V |
|
解決方案 A 4 | > 600 | V |
|
可燃性等級 |
|
| IEC 60695-11-10, -20 |
0.13 in | V-2 |
|
|
0.06 in | HB |
|
|
Electrolytical Corrosion | A1 |
| IEC 60426 |
ISO Shortname | PA12, MHR, 16-050, GF23 |
| ISO 1874 |