Crastin? HR5330HF NC010
THERMOPLASTIC POLYESTER RESIN
產(chǎn)品說明:
30% Glass Reinforced, Hydrolysis Resistant, Polybutylene Terephthalate
填料/增強(qiáng)材料 | |
添加劑 | |
特性 | |
RoHS 合規(guī)性 | |
形式 | |
加工方法 | |
多點數(shù)據(jù) | Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Modulus vs. Temperature, Dynamic (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Tensile Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
|
部件標(biāo)識代碼 (ISO 11469) | |
樹脂ID (ISO 1043) | |
密度 | 1.50 | g/cm3 | ISO 1183 |
熔融體積流量（MVR） (250°C/2.16 kg) | 0.519 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 1.0 | % |
|
流量 | 0.30 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F, 0.0787 in | 0.35 | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 0.15 | % |
|
粘數(shù) | 95.0 | cm3/g | ISO 307 |
Flow Length 3 (78.7 mil) | 14 | in |
|
拉伸模量 | 1.23E+6 | psi | ISO 527-2 |
拉伸應(yīng)力 (斷裂) | 18100 | psi | ISO 527-2 |
拉伸應(yīng)變 (斷裂) | 3.2 | % | ISO 527-2 |
彎曲模量 | 1.09E+6 | psi | ISO 178 |
彎曲應(yīng)力 | 29000 | psi | ISO 178 |
泊松比 4 | 0.34 |
| ISO 527 |
簡支梁缺口沖擊強(qiáng)度 |
|
| ISO 179/1eA |
-22°F | 5.5 | ft·lb/in2 |
|
73°F | 6.2 | ft·lb/in2 |
|
簡支梁無缺口沖擊強(qiáng)度 (73°F) | 33 | ft·lb/in2 | ISO 179/1eU |
懸壁梁缺口沖擊強(qiáng)度 |
|
| ISO 180/1A |
-40°F | 5.2 | ft·lb/in2 |
|
73°F | 6.7 | ft·lb/in2 |
|
無缺口伊佐德沖擊強(qiáng)度 (73°F) | 31 | ft·lb/in2 | ISO 180/1U |
熱變形溫度 |
|
|
|
66 psi, 未退火 | 430 | °F | ISO 75-2/B |
264 psi, 未退火 | 405 | °F | ISO 75-2/A |
玻璃轉(zhuǎn)化溫度 5 | 149 | °F | ISO 11357-2 |
維卡軟化溫度 | 419 | °F | ISO 306/B50 |
熔融溫度 5 | 437 | °F | ISO 11357-3 |
線形熱膨脹系數(shù) |
|
| ISO 11359-2 |
流動 | 1.1E-5 | in/in/°F |
|
流動 : -40 到 73°F | 1.4E-5 | in/in/°F |
|
流動 : 131 到 320°F | 8.3E-6 | in/in/°F |
|
橫向 | 8.3E-5 | in/in/°F |
|
橫向 : -40 到 73°F | 5.0E-5 | in/in/°F |
|
橫向 : 131 到 320°F | 8.1E-5 | in/in/°F |
|
表面電阻率 | 1.0E+13 | ohms | IEC 60093 |
體積電阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
介電強(qiáng)度 |
|
| IEC 60243-1 |
-- | 1100 | V/mil |
|
0.0394 in 6 | 790 | V/mil |
|
相對電容率 |
|
| IEC 60250 |
100 Hz | 4.40 |
|
|
1 MHz | 4.10 |
|
|
耗散因數(shù) |
|
| IEC 60250 |
100 Hz | 2.5E-3 |
|
|
1 MHz | 0.020 |
|
|
漏電起痕指數(shù) | 450 | V | IEC 60112 |
燃燒速率 7 (0.0394 in) | 1.2 | in/min | ISO 3795 |
UL 阻燃等級 |
|
|
|
0.030 in | HB |
| UL 94, IEC 60695-11-10, -20 |
0.06 in | HB |
| IEC 60695-11-10, -20 |
極限氧指數(shù) | 19 | % | ISO 4589-2 |
FMVSS 可燃性 | B |
| FMVSS 302 |
熔體密度 | 1.29 | g/cm3 |
|
頂出溫度 | 338 | °F |
|
Specific Heat Capacity of Melt | 0.413 | Btu/lb/°F |
|
Thermal Conductivity of Melt | 1.9 | Btu·in/hr/ft2/°F |
|
干燥溫度 | 248 | °F |
|
干燥時間 - 熱風(fēng)干燥機(jī) | 2.0 到 4.0 | hr |
|
建議的最大水分含量 | 0.040 | % |
|
加工（熔體）溫度 | 464 到 500 | °F |
|
Melt Temperature, Optimum | 482 | °F |
|
模具溫度 | 86 到 266 | °F |
|
Mold Temperature, Optimum | 176 | °F |
|
保壓 | 8700 | psi |
|
Back Pressure | As low as possible |
|
|
Drying Recommended | yes |
|
|
Hold Pressure Time | 3.00 | s/mm |
|
如需塞拉尼斯（Celanese）原廠物性表及相關(guān)文件，請聯(lián)系我司工作人員，謝謝！