Radilon? A RV500K 100 NAT
聚酰胺66
PA66 reinforced with 50% glass fiber for injection molding. Heat stabilized. Natural color.
Suitable for parts requiring very high stiffness and high strength, as in the case of applications as a replacement for metallic materials. Good thermal aging resistance.
填料/增強(qiáng)材料 | |
添加劑 | |
特性 | - 剛性高、高強(qiáng)度、良好的耐熱老化性能、熱穩(wěn)定性
|
用途 | |
RoHS 合規(guī)性 | |
外觀 | |
加工方法 | |
樹脂ID (ISO 1043) | |
密度 | 1.58 | -- | g/cm3 | ISO 1183 |
收縮率 3 |
|
|
| ISO 294-4 |
橫向流量 | 0.70 | -- | % |
|
流量 | 0.30 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
飽和, 73°F, 0.0787 in | 4.6 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.1 | -- | % |
|
拉伸模量 | 2.39E+6 | 1.81E+6 | psi | ISO 527-2/1A/1 |
拉伸應(yīng)力 (斷裂) | 34100 | 25400 | psi | ISO 527-2/1A/5 |
拉伸應(yīng)變 (斷裂) | 3.1 | 3.2 | % | ISO 527-2/1A/5 |
彎曲模量 4 | 2.18E+6 | -- | psi | ISO 178 |
彎曲應(yīng)力 4 | 52200 | -- | psi | ISO 178 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
|
| ISO 179/1eA |
-22°F | 7.6 | -- | ft·lb/in2 |
|
73°F | 8.1 | 13 | ft·lb/in2 |
|
簡(jiǎn)支梁無缺口沖擊強(qiáng)度 |
|
|
| ISO 179/1eU |
-22°F | 48 | -- | ft·lb/in2 |
|
73°F | 50 | 57 | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 491 | -- | °F | ISO 75-2/Bf |
264 psi, 未退火 | 482 | -- | °F | ISO 75-2/Af |
維卡軟化溫度 | 482 | -- | °F | ISO 306/B50 |
熔融溫度 5 | 500 | -- | °F | ISO 11357-3 |
表面電阻率 6 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
體積電阻率 6 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
漏電起痕指數(shù) (解決方案 A) | 550 | -- | V | IEC 60112 |
UL 阻燃等級(jí) (0.031 in) | HB | -- |
| UL 94 |
灼熱絲易燃指數(shù) (0.08 in) | 1290 | -- | °F | IEC 60695-2-12 |
可燃性 | 0 | -- | in/min | FMVSS 302 |
干燥溫度 - 熱風(fēng)干燥機(jī) | 176 | °F |
|
干燥時(shí)間 - 熱風(fēng)干燥機(jī) | 2.0 到 4.0 | hr |
|
Dew Point - 熱風(fēng)干燥機(jī) | -4 | °F |
|
建議的最大水分含量 | 0.15 | % |
|
加工（熔體）溫度 | 554 到 581 | °F |
|
模具溫度 | 176 到 212 | °F |
|
注射速度 | 中等偏快 |
|
|
如需蘭蒂奇原廠物性表及相關(guān)文件，請(qǐng)聯(lián)系我們工作人員，謝謝！