聚甲基丙烯酸甲酯-丙烯酸
PLEXIGLAS? Hi-Gloss FT15 black 9V022 is a special acrylic-based polymer.
With regard to its
PLEXIGLAS? Hi-Gloss FT15 9V022 shows comparable properties to those of PLEXIGLAS? standard molding compounds. In addition, PLEXIGLAS? Hi-Gloss FT15 9V022 offers the special benefit of a
Application:
PLEXIGLAS? Hi-Gloss FT15 9V022 is particularly suitable for injection molding technical components. Owing to ist superior brilliance, high-gloss (Class A) black surfaces can be obtained in.
Examples:
add-on automotive body parts
密度 | 1.19 | g/cm3 | ISO 1183 |
熔融體積流量（MVR） (230°C/3.8 kg) | 0.275 | in3/10min | ISO 1133 |
拉伸模量 | 508000 | psi | ISO 527-2/1 |
拉伸應力 (斷裂) | 7250 | psi | ISO 527-2/5 |
拉伸應變 (斷裂) | 3.1 | % | ISO 527-2/5 |
簡支梁無缺口沖擊強度 (73°F) | 8.6 | ft·lb/in2 | ISO 179/1eU |
熱變形溫度 |
|
|
|
66 psi, 未退火 | 225 | °F | ISO 75-2/B |
264 psi, 未退火 | 221 | °F | ISO 75-2/A |
玻璃轉化溫度 | 250 | °F | ISO 11357-2 |
維卡軟化溫度 | 239 | °F | ISO 306/B50 |
熱燈絲點火溫度 | 1250 | °F | IEC 60695-2-13 |
干燥溫度 | 212 | °F |
|
干燥時間 | 4.0 到 6.0 | hr |
|
加工（熔體）溫度 | 428 到 482 | °F |
|
模具溫度 | 158 到 203 | °F |
|