Plexiglas? Hi-Gloss 8N black 9V022
聚甲基丙烯酸甲酯-丙烯酸
PLEXIGLAS? Hi-Gloss 8N black 9V022 is an amorphous thermoplastic molding compound (PMMA).
Typical properties of PLEXIGLAS? molding compounds are:
Special properties of PLEXIGLAS? Hi-Gloss 8N 9V022 are:
Application:
PLEXIGLAS? Hi-Gloss 8N black 9V022 is particularly suitable for injection molding technical components. Owing to its superior brilliance, high-gloss (Class A) black surfaces can be obtained.
Examples:
add-on automotive body parts
特性 | - 高光、高強度、良好的流動性、良好耐磨損性、耐氣候影響性能良好、耐熱性高、無定形的、硬度高
|
用途 | |
外觀 | |
形式 | |
加工方法 | |
密度 | 1.19 | g/cm3 | ISO 1183 |
熔融體積流量（MVR） (230°C/3.8 kg) | 0.183 | in3/10min | ISO 1133 |
拉伸模量 | 479000 | psi | ISO 527-2/1 |
拉伸應力 (斷裂) | 11200 | psi | ISO 527-2/5 |
拉伸應變 (斷裂) | 5.5 | % | ISO 527-2/5 |
簡支梁無缺口沖擊強度 (73°F) | 9.5 | ft·lb/in2 | ISO 179/1eU |
熱變形溫度 |
|
|
|
66 psi, 未退火 | 217 | °F | ISO 75-2/B |
264 psi, 未退火 | 208 | °F | ISO 75-2/A |
玻璃轉化溫度 | 243 | °F | ISO 11357-2 |
維卡軟化溫度 | 226 | °F | ISO 306/B50 |
線形熱膨脹系數 - 流動 (32 到 122°F) | 4.4E-5 | in/in/°F | ISO 11359-2 |
可燃性等級 (0.06 in) | HB |
| IEC 60695-11-10, -20 |
干燥溫度 | < 208 | °F |
|
干燥時間 | 2.0 到 3.0 | hr |
|
加工（熔體）溫度 | 428 到 500 | °F |
|
模具溫度 | 140 到 194 | °F |
|
如需德固賽原廠物性表及相關文件，請聯系我們工作人員，謝謝！