Amodel? AS-1933 HS

Manufacturer: SOLVAY
Produced At: Import/ China
Product Category: Amodel PPA
Product No: Amodel AS-1933 HS
Product Quantity: 25KG / BAG
Product Features: Antifreeze Resistant，Chemical Resistant，Creep Resistant，Good Dimensional Stability，Good Glycol Resistance，Good，Stiffness，Heat Stabilized，High Heat Resistance，High Strength

Product information

Amodel? AS-1933 HS

Polyphthalamide

Solvay Specialty Polymers

Product Description:

Amodel? AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226°F (108°C), even when tested at 275°F (135°C).

Potential applications include a variety of automotive components such as thermostat housings, heater core endcaps, heater hose connectors, and water inlets, outlets and valves.

Black: AS-1933 HS BK 324

Filler / Reinforcement	Glass Fiber, 33% Filler by Weight
Additive	Heat Stabilizer
Features	Antifreeze Resistant,Chemical Resistant,Creep Resistant,Good Dimensional Stability,Good Glycol Resistance,Good Stiffness,Heat Stabilized,High Heat Resistance,High Strength
Uses	Automotive Applications,Automotive Under the Hood,Housings,Industrial Applications,Industrial Parts,Machine/Mechanical Parts,Metal Replacement,Power/Other Tools,Thick-walled Parts,Valves/Valve Parts
RoHS Compliance	RoHS Compliant
Appearance	Black
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1)

Physical	Nominal Value	Unit	Test Method
Density	1.45	g/cm3	ISO 1183/A
Molding Shrinkage			ASTM D955
Flow	2.0E-3	in/in
Across Flow	6.0E-3	in/in
Water Absorption (24 hr)	0.21	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
--	1.70E+6	psi	ASTM D638
-- 3	1.10E+6	psi	ASTM D638
--	1.83E+6	psi	ISO 527-2
Tensile Strength
Break	32000	psi	ASTM D638
Break 3	11000	psi	ASTM D638
Break	30700	psi	ISO 527-2
Tensile Elongation (Break)	2.5	%	ASTM D638, ISO 527-2
Flexural Modulus
--	1.56E+6	psi	ASTM D790
--	1.54E+6	psi	ISO 178
Flexural Stress
--	44800	psi	ISO 178
Yield	45400	psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	4.8	ft·lb/in2	ISO 179/1eA
Charpy Unnotched Impact Strength	36	ft·lb/in2	ISO 179/1eU
Notched Izod Impact
--	1.7	ft·lb/in	ASTM D256
-- 3	1.0	ft·lb/in	ASTM D256
--	4.5	ft·lb/in2	ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
264 psi, Unannealed	530	°F	ASTM D648
264 psi, Unannealed	532	°F	ISO 75-2/Af
Melting Temperature	594	°F	ISO 11357-3

Injection	Nominal Value	Unit
Drying Temperature	250	°F
Drying Time	4.0	hr
Suggested Max Moisture	0.030 to 0.060	%
Hopper Temperature	175	°F
Rear Temperature	580 to 605	°F
Front Temperature	600 to 625	°F
Processing (Melt) Temp	610 to 650	°F
Mold Temperature	275	°F
Injection Notes
Storage: Amodel? compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel? resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel? processing guide.