Ultrason? E KR 4113

Manufacturer: BASF
Produced At: Europe / China
Product Category: Polyethersulfone
Product No: Ultrason EKR 4113
Product Quantity: 25KG / BAG
Product Features: Carbon\Graphite\PTFE,30% Filler by Weight

Product information

Ultrason? E KR 4113

Polyethersulfone

BASF Corporation

Product Description:

Compound based on PES with 30 % filler. The filler system, a mixture of carbon fibres, graphite and PTFE powder, considerably improves Ultrason tribological properties. In addition, this product has a very small expansion coefficient and low tendency to swell in hot oils.

Filler / Reinforcement	Carbon\Graphite\PTFE, 30% Filler by Weight
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Extrusion、Injection Molding
Resin ID (ISO 1043)	PESU+ PTFE-(CF+CD)

Physical	Nominal Value	Unit	Test Method
Density	1.48	g/cm3	ISO 1183
Apparent (Bulk) Density	0.70 to 0.80	g/cm3
Melt Volume-Flow Rate (MVR) (360°C/10.0 kg)	0.610	in3/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Across Flow	0.46	%
Flow	0.31	%
Water Absorption			ISO 62
Saturation, 73°F	1.5	%
Equilibrium, 73°F, 50% RH	0.50	%
Viscosity Number 2	56.0	cm3/g	ISO 307
Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness (H 961/30)	26100	psi	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1.60E+6	psi	ISO 527-2
Tensile Stress (Break)	16700	psi	ISO 527-2
Tensile Strain (Break)	1.5	%	ISO 527-2
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-22°F	2.4	ft·lb/in2
73°F	3.1	ft·lb/in2
Charpy Unnotched Impact Strength			ISO 179/1eU
-22°F	9.5	ft·lb/in2
73°F	11	ft·lb/in2
Notched Izod Impact Strength			ISO 180/A
-22°F	2.6	ft·lb/in2
73°F	3.1	ft·lb/in2

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (264 psi, Unannealed)	433	°F	ISO 75-2/A
Glass Transition Temperature 3	437	°F	ISO 11357-2
CLTE - Flow
73 to 176°F	6.1E-6	in/in/°F	ISO 11359-2
356°F	7.2E-6	in/in/°F	DIN 53752

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	4.0E+3	ohms	IEC 60093
Volume Resistivity	9.0E+5	ohms·cm	IEC 60093
Electric Strength	200	V/mil	IEC 60243-1

Injection	Nominal Value	Unit
Drying Temperature	284	°F
Drying Time	4.0	hr
Suggested Max Moisture	0.020	%
Hopper Temperature	176	°F
Rear Temperature	662	°F
Middle Temperature	680	°F
Front Temperature	698	°F
Nozzle Temperature	698	°F
Processing (Melt) Temp	662 to 734	°F
Mold Temperature	302 to 374	°F
Screw Speed	< 709	in/min