Plexiglas? Satinice df33 zk6BR
Polymethyl Methacrylate Acrylic
PLEXIGLAS? Satinice df33 zk6BR, based on PLEXIGLAS? Resist zk6BR, is an impact modified molding compound characterized by diffuse scattering of light.
Typical properties of impact modified PLEXIGLAS? molding compound are
Extruded parts from PLEXIGLAS? Satinice df33 zk6BR are characterized by the following special properties:
Application:
Used for (Co-) extruding profiles and sheets for the construction, furniture and automotive industry, but also for injection molding items for lighting engineering applications.
Examples:
applications that call for light diffusion combined with optimum transmission and velvet matt surface appearance is desired.
Features | - HHigh Hardness，High Impact Resistance，High Light Diffusion，High Light Transmission，Impact Modified，Medium Gloss，Weather Resistant
|
Uses | - Automotive Applications，Construction Applications，Furniture，Lighting Diffusers，Profiles，Sheet
|
Appearance | |
Forms | |
Processing Method | - Coextrusion，Extrusion，Injection Molding
|
Density | 1.16 | g/cm3 | ISO 1183 |
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 0.0854 | in3/10min | ISO 1133 |
Tensile Modulus | 290000 | psi | ISO 527-2/1 |
Tensile Stress (Yield) | 6530 | psi | ISO 527-2/50 |
Tensile Strain (Yield) | 4.0 | % | ISO 527-2/50 |
Nominal Tensile Strain at Break | 25 | % | ISO 527-2 |
Charpy Unnotched Impact Strength (73°F) | 19 | ft·lb/in2 | ISO 179/1eU |
Heat Deflection Temperature |
|
|
|
66 psi, Unannealed | 210 | °F | ISO 75-2/B |
264 psi, Unannealed | 205 | °F | ISO 75-2/A |
Vicat Softening Temperature | 210 | °F | ISO 306/B50 |
CLTE - Flow (32 to 122°F) | 5.1E-5 | in/in/°F | ISO 11359-2 |
Glow Wire Ignition Temperature | 1290 | °F | IEC 60695-2-13 |
Transmittance 2 | 67.0 | % | ISO 13468-2 |
Half-Value Angle | 36.0 | ° | DIN 5036 |
Scattering Power | 0.490 |
| DIN 5036 |
Drying Temperature | < 185 | °F |
|
Drying Time | 2.0 to 3.0 | hr |
|
Melt Temperature | 446 to 500 | °F |
|
Die Temperature | 446 to 500 | °F |
|